Silicone Primer CL-26AB-24 LSR Silicone overmolding Aluminium CL-26AB-24, Silicone primer is applied on unvulcanized addition type, peroxide-system/ platinum -system silicone overmold onto hard substrates like metal, alum
Tel: +0086 -180 9899 4276 | ||
Fax: +86 755 8147 8872 | ||
E-mail: sales@bondsil.com |
CL-26AB-24, Silicone primer is applied on unvulcanized addition type, peroxide-system/ platinum -system silicone overmold onto hard substrates
like metal, aluminium ,PA, PET(Polyethylene terephthalate glycol ester)
lsr silicone overmolding aluminium
High Tear Strength
The Silicone rubber is damaged when tearing from Aluminium
LSR Silicone overmolding Aluminium
Adhesion Strength is over 2Mpa, No bonding failure
ISO9001, SGS certified
No Bubbles
Making your silicone products 99% good products rate
No primer traces after the silicone products is made
Labour costs saving
Easy processing, Can dip dry, No corrosion to Aluminium
Stable Quality
3 Times standard tests
zero silicone falls aparts from substrates
High Temperature Tolerance
Temperature tolerance for Second-cure of silicone rubber
at 200 degrees for 4hours
Color: Transparent Liquid or Gel
Component: A:Gel, B: Platinum Catalyst
Mixing Ratio: A:B=1:1(Use up within 4hours after mixture)
1, Treat the substrates with blast sanding, polishing or wash with industrial alcohol.
2, Mix completely the A and B with ratio 1:1 and apply the primer by dipping, brushing, spraying or silk screen printing method.
3, Leave dry in room temp for 30 minutes or baking at 110-130℃ for 15-20mintes.
4, The primer treated substrates are processed within that day.
5, Foward the unvulcanized silicone rubber with primer-coated substrates in mouding process or hot air vulcanization.
1, Please cap its cover immediately after use to avoid volatilization.
2, Store the used and unused adhesive in separate way to lengthen the shelf life.
3, After the primer coated on the substrates, leave it volatilize completely before entering the mold. Otherwise, there will be bubbles in the finished products
4, Wash clean the substrates to remove dirts or oil to avoid bad adhesion.
5, The PA substrates is water-absorbent, it must be dried up before molding with silicone. Better bake with 150 degrees for 1-2hours.
+0086 -180 9899 4276 Gary Lee
+0086 -135 0281 9396 Wendy Wei
+0086 -138 2374 7978 Kyler Yang
+86 755 8147 8872
H Building ,Xinwei The 3rd Industrial Park,Dalang Street,Longhua New District , Shenzhen City ,Guangdong Province ,China